Waste plastic for increasing softening point of pitch and specific surface area of activated carbon based on the petroleum residue

서지정보

ㆍ발행기관 : 한국탄소학회 ㆍ수록지정보 : Carbon letters / 31권 / 5호
ㆍ저자명 : Cheol Hwan Kwak, Sang Wan Seo, Min Il Kim, Yun Suk Huh, Ji Sun Im

목차

Abstract
1 Introduction
2 Experimental
2.1 Materials
2.2 Pitch synthesis using PFO and PET
2.3 Pitch activation using KOH
2.4 Analysis of characteristics
3 Results
3.1 Change of softening point depending on PET addition
3.2 Pore characteristics of activated carbon products prepared by using pitch synthesized under different conditions
4 Discussion
4.1 Pitch pyrolysis characteristics depending on pet addition
4.2 Change in molecular weight of pitch depending on PET addition
5 Conclusion
Acknowledgements
References

영어 초록

Pyrolysis fuel oil (PFO) is used for the manufacturing of high-purity pitch for carbon precursor due to its high carbon content, high aromaticity, and low heterogeneous element and impurity content. Pitch is commonly classified with its softening point, which is most considerable physical property affecting to various characteristics of the carbon materials based on pitch, such as electrical and thermal conductivity, mechanical strength, and pore property. Hence, the softening point should be controlled to apply pitch to produce various carbon materials for different applications. Previous studies introduce reforming process under high pressure and two step heat treatment for the synthesis of pitch with high softening point from PFO. These methods lead to a high process cost; therefore, it is necessary to develop a process to synthesize the pitch with high softening point by using energy effective process at a low temperature. In this study, waste polyethylene terephthalate (PET) was added to control the softening point of PFO-based pitch. The pitch synthesized by the heat treatment with the addition of PET showed the softening point higher than that of the pitch synthesized with only PFO. The softening point of PFObased pitch synthesized at 420 °C was 138.3 °C, while that of the pitch synthesized by adding PET under the same process conditions was 342.8 °C. It is proposed that the effect of the PET addition on the increase in the softening point was due to the radicals generated from thermal degradation of PET. The radicals from PET react with the PFO molecules to promote the polymerization and finally increase the molecular weight and softening point of the pitch. In addition, activated carbon was prepared by using the pitch synthesized by adding PET, and the results showed that the specific surface area of the activated carbon increased by the addition of PET. It is expected that the pitch synthesis method with PET addition significantly contributes to the manufacture of pitch and activated carbon.