· 발행기관 : 한국기계기술학회
· 수록지 정보 : 한국기계기술학회지 / 25권 / 1호
· 저자명 : 최선순
영어초록
The purpose of this research is to investigate the statistical behavior of fatigue crack propagation(FCP) in magnesium alloy AZ31. FCP tests have been performed on compact specimens of AZ31 at load ratio conditions and maximum fatigue load conditions to obtain statistical data of FCP. It was found that the variability of fatigue crack propagation rate was significantly large at initial stage of FCP and gradually became smaller as the fatigue crack propagated. The finding of the study showed that increasing the load ratio could increase the variability of fatigue crack propagation rate at initial FCP stage. The samller the load ratio, the higher the fatigue crack propagation rate at initial stage. It was also found that the load ratio is a factor affecting the fatigue crack propagation rate in magnesium alloy.참고자료
· 없음태그
-
자료후기
Ai 리뷰지식판매자의 자료는 는 매번 기대 이상의 정보를 제공합니다. 특히, 다양한 주제를 깊이 있게 다루고 있어 학습할 때 지루함을 느끼지 않습니다. 학업에 적용할 수 있는 유용한 팁들이 많아, 학습한 내용을 실제로 활용할 수 있어 매우 만족스럽습니다. 앞으로도 계속해서 이 지식판매자의 자료를 이용할 생각입니다!
-
자주묻는질문의 답변을 확인해 주세요
꼭 알아주세요
-
본 학술논문은 (주)코리아스칼라와 각 학회간에 저작권계약이 체결된 것으로 AgentSoft가 제공 하고 있습니다.
본 저작물을 불법적으로 이용시는 법적인 제재가 가해질 수 있습니다. -
해피캠퍼스는 구매자와 판매자 모두가 만족하는 서비스가 되도록 노력하고 있으며, 아래의 4가지 자료환불 조건을 꼭 확인해주시기 바랍니다.
파일오류 중복자료 저작권 없음 설명과 실제 내용 불일치 파일의 다운로드가 제대로 되지 않거나 파일형식에 맞는 프로그램으로 정상 작동하지 않는 경우 다른 자료와 70% 이상 내용이 일치하는 경우 (중복임을 확인할 수 있는 근거 필요함) 인터넷의 다른 사이트, 연구기관, 학교, 서적 등의 자료를 도용한 경우 자료의 설명과 실제 자료의 내용이 일치하지 않는 경우
문서 초안을 생성해주는 EasyAI